核燃料包壳作为反应堆的核心结构材料,在长期服役过程中会发生高温蠕变现象,导致材料机械性能降低,严重影响核能安全。因此探讨了FeCrAl合金薄壁管环向蠕变速率沿径向的分布特征。
As the core structural material of the reactor, the nuclear fuel cladding undergoes high-temperature creep during the long-term service process, resulting in a decrease in the mechanical properties of the material and seriously affecting the safety of nuclear energy. Therefore, The hoop creep rates of FeCrAl thin tubes along the radial direction is discussed.