The product film formed on Ni-advanced weathering steel in a tropical marine environment was investigated in detail through outdoor exposure by using diverse surface analysis techniques combined with electrochemical impedance spectroscopy and scanning kelvin probe measurements. The results showed that the product film was mainly composed of nanophasic goethite in the inner layer and maghemite, akaganeite, and hematite in the outer layer. Moreover, the resistance to atmospheric corrosion gradually increased from the outermost product film to the innermost film. Ni was significantly enriched in the inner layer in the form of the spinel phase NiFe2O4, which transformed lepidocrocite to fine-grained goethite, withstood the invasion of chloridion, and improved the corrosion potential of the product film in a tropical marine atmosphere.