本发明公开超宽厚壁X80级管线用热轧钢板及其生产方法。钢中含有,C:0.03%~0.05%、Si:0.16%~0.28%、Mn:1.50%~1.75%、Nb:0.05%~0.08%、Ti:0.012%~0.025%、Cr:0.10%~0.25%、V:0.01%~0.04%、Mo≤0.1 9%、Ni≤0.20% 、Cu≤0.14%、Al≤0.020%、P≤0.013%、S≤0.0015%、O:0.0005%~0.0020%、N:0.001%~0.004%、Ca:0.0010% ~0.0045%且满足Ca/S≥1.6,Mo+Ni+Cr+Cu:0.40%~0.65%,余量为铁和不可避免的杂质;粗轧开轧温度1070~1150℃,精轧开轧温度820~860℃,终轧温度760~780℃,冷却温度730~770℃,钢板宽度>4000mm,厚度>25mm,低温韧性良好、屈强比低。
The invention discloses hot rolled steel plate for super wide and thick wall X80 grade pipeline and a production method thereof. In steel, C: 0.03% ~ 0.05%, Si: 0.16% ~ 0.28%, Mn: 1.50% ~ 1.75%, Nb: 0.05% ~ 0.08%, Ti: 0.012% ~ 0.025%, Cr: 0.10% ~ 0.25%, V: 0.01% ~ 0.04%, Mo≤0.19%, Ni≤0.20%, Cu≤0.14%, Al≤0.020%, P≤0.013%, S≤0.0015%, O: 0.0005% ~ 0.0020%, N: 0.001% ~ 0.004%, Ca: 0.0010% ~ 0.0045% and Ca/S≥1.6, Mo+Ni+Cr+Cu: 0.40% ~ 0.65%, residual iron and unavoidable impurities. Rough rolling opening temperature is 1070 ~ 1150℃, finish rolling opening temperature is 820 ~ 860℃, finishing rolling temperature is 760 ~ 780℃, cooling temperature is 730 ~ 770℃, the width of the steel plate is more than 4000mm, the thickness is more than 25mm, the steel plate has excellent low temperature toughness and low yield ratio.