本发明公开了一种确定管线钢DWTT 减薄试样试验温度的方法,属于力学性能测试领域。本发明的方法,包括以下:1)取X70 或X80 管线钢,得到不同温度下的剪切面积百分数;拟合,得到SA%-T,得到FATT85%;2)减薄试样,得到一系列壁厚的试样,得到相应壁厚下温度与剪切面积百分数的对应值;将数据分别进行拟合,得到一系列试样的SA%-T 拟合曲线;根据SA%-T 拟合曲线,得到不同试样的FATT85%;3)将1)和2)中任意两个试样的壁厚和FATT85%求差,得到壁厚减薄量和温度降低量,将两个量进行回归,得到拟合曲线;4)进行试样测试时,根据试样壁厚减薄量和3)的曲线获取相应的温度降低量。
The invention discloses a method for determining the test temperature of pipeline steel DWTT thinning sample, belonging to the field of mechanical property test. The method of the invention comprises the following steps: Taking X70 or X80 pipeline steel to obtain the percentage of shear area at different temperatures; Fitting, SA% -T, FATT85%; Thin the sample to obtain a series of samples with wall thickness, and obtain the corresponding value of temperature and shear area percentage under the corresponding wall thickness; The data were fitted separately to obtain the SA% - T fitting curves of a series of samples; According to SA% - T fitting curve, fatt85% of different samples are obtained; Calculate the difference between the wall thickness and FATT85% of any two samples in 1) and 2) to obtain the wall thickness reduction and temperature reduction, and regress the two quantities to obtain the fitting curve; When testing the sample, obtain the corresponding temperature reduction according to the wall thickness reduction of the sample and the curve of 3).