名称 : 不同条件下氧化的TC4合金表面的XRD图谱
英文名称 : XRD patterns of surface of TC4 alloy oxidized under various conditions
材料 : 146
委托单位 : 北京科技大学
实验单位 : 北京科技大学
实验方法 : XRD测试
实验设备 : X射线衍射仪
实验条件 : 常温
说明 : Figure 5 presents the XRD patterns of the specimens oxidized under various conditions. The oxidized surface of the alloy consisted mainly of rutile-type TiO2
and a small amount of Al2O3 and TiVO4 (a solid solution of TiO2 and VO2). In contrast to the previous reports , there were no Ti diffraction peaks in the
XRD pattern because the scale was very thick after severe oxidation and the X-rays could not penetrate the oxides to detect the Ti substrate.
英文说明 : Figure 5 presents the XRD patterns of the specimens oxidized under various conditions. The oxidized surface of the alloy consisted mainly of rutile-type TiO2
and a small amount of Al2O3 and TiVO4 (a solid solution of TiO2 and VO2). In contrast to the previous reports , there were no Ti diffraction peaks in the
XRD pattern because the scale was very thick after severe oxidation and the X-rays could not penetrate the oxides to detect the Ti substrate.
重点项目名称 : 低成本高耐蚀钛及钛合金管材与高品质钛带制造技术开发及应用