按照Mo-0.55Ti-0.12Zr-C组分配料方式，其中碳含量分别按照0.04%、0.08%、0.10%、0.12%的比例进行混料，同炉高温烧结后取样检测，取样时先用磨床磨去表面1mm，之后再用砂纸抛光，然后取样分别采用TC600氧氮分析仪和C600碳分析仪检测合金中的氧含量和碳含量。观察碳含量对TZM钼合金氧含量的影响。

According to the mo-0.55ti-0.12zr-c component proportioning method, the carbon content shall be mixed according to the proportion of 0.04%, 0.08%, 0.10% and 0.12% respectively. After high-temperature sintering in the same furnace, samples shall be taken for testing. During sampling, the surface shall be ground off by a grinder, and then polished with sandpaper, Then take samples and use TC600 oxygen nitrogen analyzer and c600 carbon analyzer to detect the oxygen content and carbon content in the alloy. The effect of carbon content on oxygen content of TZM molybdenum alloy was observed.