利用粉末冶金法制得了板型规整的纯钼烧结坯，在Gleeble-1500型热模拟实验机上对纯钼板坯进行热压缩变形实验，变形温度为1100°C～1300 °C、变形速率为0.01～10 s^-1、真应变为0.3～0.6。不同形变条件下断口场发射扫描电子显微镜下进行观察分析。

A pure molybdenum sintered compact with a regular plate shape was prepared by powder metallurgy. The pure molybdenum slab was subjected to a thermal compression deformation experiment on the Gleeble-1500 thermal simulation test machine. The deformation temperature was 1100°C～1300°C, and the deformation rate was 0.01～ 10 s-1, the true strain is 0.3 to 0.6. Observation and analysis under different deformation conditions under a fracture field emission scanning electron microscope.