公开了双相不锈钢中板表面处理方法,其包括:a )对所述双相不锈钢中板表面进行抛丸处理;以及b)对经过抛丸处理的双相不锈钢中板表面进行连续酸洗;其中所述连续酸洗包括第一连续酸洗和第二连续酸洗,所述第一连续酸洗使用单一酸,所述第二连续酸洗使用硝酸和氢氟酸的混酸,其中所述硝酸的浓度为30g/L-80g/L,所述氢氟酸的浓度为60g/L-85g/L,基于质量百分比, 所述双相不锈钢含有C≤0 .030%,Si≤1 .00%, Mn≤2 .0 0% ,P≤0 .0 3 0% ,S≤0 .0 2 0% , Cr 21 .00%-23 .00%,Ni 4 .50%-6 .50%,Mo 2 .50%-3 .50%,N 0 .14%-0 .20%,余量为铁及其他不可避免的杂质。使用本申请的方法实现了高效连续酸洗,表面色泽一致,满足了高端领域对钢板的高表面质量要求。
A surface treatment method for a duplex stainless steel mid-plate is disclosed, which includes: a) performing shot blasting on the surface of the duplex stainless steel mid-plate; and b) performing continuous pickling on the surface of the dual-phase stainless steel mid-plate after shot blasting; Wherein the continuous pickling includes a first continuous pickling and a second continuous pickling, the first continuous pickling uses a single acid, and the second continuous pickling uses a mixed acid of nitric acid and hydrofluoric acid, wherein the nitric acid The concentration of the hydrofluoric acid is 30g/L-80g/L, the concentration of the hydrofluoric acid is 60g/L-85g/L, based on mass percentage, the duplex stainless steel contains C≤0.030%, Si≤1.00% , Mn≤2.0 0%, P≤0.03 0%, S≤0.020%, Cr 21.00%-23.00%, Ni 4.50%-6.50%, Mo 2.50%-3.50%, N 0.14%-0.20%, the balance is iron and other unavoidable impurities. Using the method of the present application, high-efficiency continuous pickling is realized, and the surface color is consistent, which meets the high surface quality requirements of high-end fields for steel plates.