名称 : DZ2(连铸)光滑试样±420MPa疲劳寿命
英文名称 : The fatigue life of DZ2(continuous casting) smooth specimen is ±420MPa
材料 : 877
委托单位 : 钢铁研究总院
实验单位 : 国家钢铁产品质量监督检验中心
实验方法 : 疲劳试验
实验设备 : 微机控制高频疲劳试验机-QBG-100
实验条件 : 室温
说明 :

疲劳性能测试参考GB/T 4337-2015进行试验，在微机控制高频疲劳试验机-QBG-100上开展实验，加载频率为 80 Hz。为了减小疲劳试样在试验过程中内摩擦导致的发热效应，本实验采用压缩空气对试样进行冷却，并采用150ns间隙加载。利用升降法得到疲劳试验的散点图，绘制S-N曲线，继而测得试验钢的疲劳极限。

英文说明 :

The fatigue performance test was carried out according to GB/T 4337-2015. The test was carried out on the microcomputer controlled high frequency fatigue testing machine -QBG-100, and the loading frequency was 80 Hz. In order to reduce the heating effect caused by internal friction in the fatigue sample during the test, compressed air was used to cool the sample and 150ns clearance loading was used. Scatter diagram of fatigue test was obtained by lifting method, s-N curve was drawn, and then the fatigue limit of test steel was measured.

数据来源 : 分析测试报告
附件下载
重点项目名称 : 苛刻环境下铁路车辆关键部件用钢-高速车轴钢基础研究数据集
材料
委托单位
实验单位
实验方法
实验设备
实验条件
数据来源
重点项目名称
网站导航 | 版权声明 | 法律法规 | 联系我们
版权所有：国家材料环境腐蚀平台 京ICP备13025191号 京公网安备11010802026268号

关于国家科技资源服务平台

国家科技基础条件平台中心是科技部直属事业单位，致力于推动科技资源优化配置，实现开放共享，其主要职责是：承担国家科技基础条件平台建设项目的过程管理和基础性工作；承担国家科技基础条件平台建设发展战略、规范标准、管理方式、运行状况和问题的研究，以及国际合作与宣传、培训等工作；承担科技基础条件门户系统的建设与运行管理工作；参与对在建和已建国家科技基础条件平台项目的考核评估和运行监督工作。

国家科技资源服务平台相关网站


国家材料腐蚀与防护科学数据中心
国家高能物理科学数据中心
国家基因组科学数据中心
国家微生物科学数据中心
国家空间科学数据中心

国家天文科学数据中心
国家对地观测科学数据中心
国家极地科学数据中心
国家青藏高原科学数据中心
国家生态科学数据中心

国家冰川冻土沙漠科学数据中心
国家计量科学数据中心
国家地球系统科学数据中心
国家人口健康科学数据中心
国家基础学科公共科学数据中心

国家农业科学数据中心
国家林业和草原科学数据中心
国家气象科学数据中心
国家地震科学数据中心
国家海洋科学数据中心